Effect of toothbrushing on surface roughness, gloss, and topography of polished and glazed ultra-translucent zirconia

Abstract

Purpose: This study evaluated the effect of toothbrushing cycles on surface roughness (Ra), gloss (GU), and morphology of two zirconia finishing and polishing protocols. Materials and methods: An ultra-translucent zirconia disc was sectioned into rectangular plates (12 mm × 7 mm × 3 mm) and divided into two groups according to the polishing and finishing system used (diamond rubber abrasive/DRA or glazing/GLA). Bovine enamel (BEN) plates with the same dimensions were used as a Control. Specimens of zirconia and enamel were analyzed for Ra and GU (n = 11) and surface morphology by scanning electron microscopy (n = 3) before toothbrushing (baseline) and after 15,000 and 30,000 toothbrushing cycles. Ra and GU data were analyzed by ANOVA two-way and post-hoc Tukey's test (α = 0.05), while the surface morphology was analyzed qualitatively. Results: The Ra decreased significantly after 30,000 toothbrushing cycles for DRA and GLA zirconia ceramics. DRA showed a higher GU at the baseline, after 15,000 and 30,000 toothbrushing cycles than GLA and BEN. Toothbrushing polished the zirconia, creating a smooth surface, while no changes were observed for BEN. Conclusions: The increase in toothbrushing cycles (30,000) changed the surface roughness of DRA and GLA zirconia ceramics. DRA zirconia presented the highest GU, which did not change with toothbrushing.